脉冲激光与电弧布置方式对铝合金焊接熔滴过渡与焊缝形貌的影响

以2219铝合金为基板，研究了不同脉冲激光-电弧布置方式下的熔滴过渡与焊缝形貌特征，分析了熔深增加的机理. 结果表明，当脉冲激光照射母材时，脉冲激光主要提供对母材的热输入，母材温度的增加有助于促进熔滴铺展，稳定熔滴过渡过程；当脉冲激光照射熔滴缩颈时，主要提供对熔滴的力输入，蒸发反力的作用下形成"一脉一滴"，显著提高熔滴过渡频率与熔滴飞行速度，增加了熔滴对熔池的冲击力，熔深增加；当脉冲激光交替的照射熔池和熔滴时，一方面能够对母材进行加热，有助于熔滴的铺展，另一方面能够提高熔滴过渡频率，提高焊缝的均匀性.     

超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

针对100 mm超厚板TC4钛合金电子束焊接接头，采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性，分析接头的显微组织和断口形貌，对接头的腐蚀机制进行研究. 结果表明，室温条件下应变速率为ε=1×10-6 s-1时，母材在海水中未表现出应力腐蚀敏感性；焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解，产生氢吸附，导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积，进而使裂纹在更低的应力水平下发生扩展.     

On the application of remote sensing towards the estimation of cultivated land lost to urbanization

In this research work, a 40-km² SPOT-5 High-Resolution Imagery (HRI) of the Warsak locality in district Peshawar, Pakistan, was utilized to approximate the quantity of cultivated land lost to urbanization, due to the construction of new homes and buildings. The imagery from a period of 2005 to 2015 for wheat crop was taken, specifically during the months of March and June when the crop is rich green and golden ripe respectively. eCognition ® program’s Object-Oriented Classification Method (OOCM) was employed for recognition of land versus buildings. Nearest Neighbour (NN), Support Vector Machine (SVM), Decision Trees (DT) and Random Forests (RF) were utilized for the classification process. The results demonstrated that the urbanized area had increased by approximately 28 per cent in the area considered. Moreover, the efficacy of the proposed method is depicted by an accuracy of 97.9 per cent and a Kappa Statistics of 0.975 for the SVM classifier.     

0Cr17Ni4Cu4Nb传感器断裂原因分析

某力学传感器在出厂检验流程中发生断裂失效,为了确定失效原因,防止此类失效事件再次发生,实验对该传感器的力学性能、金相组织和断口形貌进行了分析,确定了断裂原因。结果表明,传感器的失效模式为氢致延迟开裂,材料中氢含量偏高和开裂位置机加工质量较差是导致传感器发生氢致开裂的主要原因。结合失效原因,提出了改进措施。     

Methane bi-reforming over boron-doped Ni/SBA-15 catalyst: Longevity evaluation

A highly active and stable boron-promoted catalyst was successfully prepared by using the sequential incipient wetness impregnation technique and examined for methane bi-reforming reaction. The initial investigation found that the NiO and B₂O₃ particles were dispersed on the outer surface of the high surface area SBA-15 support. In addition, the catalytic activity was increased linearly with the tested reaction temperature due to the endothermic nature of the reaction. In fact, the catalyst achieved the CH₄ conversion and H₂/CO molar ratio of approximately 67.3% and 2.7, respectively at 1073 K. The resulting product ratio is highly suitable for downstream Fischer-Tropsch (FT) synthesis. The B-promoted catalyst showed the lowest degree of catalyst deactivation (4%) at 1023 K. Additionally, the XPS measurements unveiled that the boron facilitates the adsorption of CO₂ by donating electrons to the neighbouring Ni cluster and thus improved its catalytic performance. Furthermore, Raman and XRD analysis revealed that the boron promotion on 10%Ni/SBA-15 could prevent the reoxidation and deposition of carbonaceous species.     

Mg-5Y-3Sm-0.8Ca-0.5Sb合金的高温蠕变行为

采用蠕变实验和理论计算,研究了时效态Mg-5Y-3Sm-0. 8Ca-0. 5Sb合金在250～300℃和50～70 Pa条件下的蠕变行为。结果表明,该合金具有良好的抗高温蠕变性能,其在300℃和70 MPa下的稳态蠕变速率为3. 28×10-8s-1。在50～70 MPa的应力下,当温度由250℃升到300℃时,应力指数由2. 30变为3. 22;在250～300℃的温度下,当应力由50 MPa升到70 MPa时,蠕变激活能由65. 4 kJ/mol变为81. 0 kJ/mol。     

Improved Corrosion Resistance of Selective Laser Melted Ti–5Cu Alloy Using Atomized Ti–5Cu Powder

The different types of metal powder used for selective laser melting(SLM) process would cause distinct corrosion behavior due to the uniformity of the obtained microstructure.The SLM-produced Ti–5Cu alloy using atomized Ti–5Cu metal powder(SLMed Ti–5Cu) in this work reveals a relatively uniform microstructure with overwhelming acicular α/α′ phase and shows great advantages on corrosion resistance compared with the SLM-produced Ti–5Cu alloy using the mixture powder(SLMedM Ti–5Cu).The effect of the micro-galvanic cells decreases due to the undetectable Ti_2Cu phase in the microstructure of the SLMed Ti–5Cu.An apparent passivation behavior was observed for SLMed Ti–5Cu instead of severe pitting phenomenon for the SLMed-M Ti–5Cu.The charge transfer resistance of SLMed Ti–5Cu in this work is 10.09 ± 2.63 MΩ cm~2, which is significantly higher than that of SLMed-M Ti–5Cu(4.76 MΩ cm~2).The above result indicates the atomized Ti–5Cu powder plays an important role in the formation of the uniform microstructure of SLMed product, thereby enhancing its corrosion resistance in Hank's solution at 37 ℃.     

吐哈盆地葡北地区“两宽一高”地震勘探技术及应用效果

吐哈盆地台北凹陷圈闭落实的准确度和储层分布预测的精度一直是制约该区油气发现的关键因素。通过可控震源“两宽一高”地震采集、OVT域时间偏移、地质导向深度偏移初始模型建立及各向异性深度偏移迭代处理，在地震资料的信噪比、频带宽度和分辨率等方面明显提高的基础上，以高精度层序地层学为指导，基于高分辨率地震资料与钻井、测井资料的综合分析，识别出侏罗系6个三级层序，在三级层序格架内将研究区七克台组底部和三间房组顶部砂体识别为两个连续上升半旋回四级层序；通过构造几何属性分析及精细构造分析，揭示了本区“四带、两凹”的构造格局及形成机制；以宽频带多种反演技术为手段，对含油气层段的七克台组和三间房组砂体分布进行了预测；在综合构造分析、储层分析和油藏成藏规律分析的基础上，提出本区油气沿构造带脊线聚集，断裂系统是油气运移的优势路径，七克台组、三间房组储层在葡北构造带发育，向玉果构造带和胜北次凹减薄尖灭，葡北构造带与玉果构造带结合部位的，具有鼻状构造背景的岩性圈闭是获得油气突破的有利地区。     

耐蚀合金中TiN析出机制

摘要：TiN颗粒尺寸及其分布对耐蚀合金性能有明显的影响，因此有必要对TiN在铸坯中的分布及其析出行为进行研究。采用扫描电镜(SEM)、金相显微镜（OM）观察了TiN夹杂物在铸坯中的分布、尺寸及其形貌；基于热力学和动力学理论分析了耐蚀合金铸坯中TiN夹杂物的析出时机及其尺寸，结合试验结果和理论计算明确了TiN夹杂物在凝固后铸坯中的位置和尺寸与析出时机的关系，为控制TiN夹杂物提供理论指导。结果表明，冶炼过程中析出的TiN夹杂物尺寸较大，在凝固过程中被枝晶吞没，位于铸坯枝晶内和等轴晶内；微观偏析计算结果表明，在凝固分数为0.55时，TiN开始析出，最开始析出TiN夹杂物的逐渐长大，长大后的TiN易于被二次枝晶吞没，最终位于铸坯中的枝晶间和等轴晶内，后期析出的TiN则在枝晶间和等轴晶间。固相中析出的TiN夹杂物长大较慢，尺寸细小，最终位于奥氏体晶界。     

两种3D打印用雾化Ti-6Al-4V粉末的对比研究

本研究分别利用水冷铜坩埚真空感应熔炼气雾化(VIGA-CC)和等离子旋转电极(PREP)两种技术制备出球形Ti-6Al-4V合金粉末,作者利用SEM、同步辐射CT扫描-三维重建和氩气含量测试等分析手段对不同粒径的Ti-6Al-4V合金粉末的孔洞缺陷和氩气含量、硬度值进行了表征。实验结果表明, VIGA-CC粉末粒度分布宽,细粉收得率较多,粉末粒度分布在40~180 μm之间, PREP粉末的粒度分布较窄,主要集中在110~180 μm之间；金属粉末内部的孔隙率、气体含量和孔尺寸随着粉末粒度的增大而增大,且同一粒径范围内VIGA-CC粉末的气孔概率多于PREP粉末；随着粉末粒径减小,粉末截面组织逐渐细化,其硬度值逐渐升高,整体上VIGA-CC粉末硬度值高于PREP粉末。